BD426 desulfurization slurry recycle pump pipeline ceramic lining repair anti wear corrosion chemical resistant coating:

Packing specification:
Two component,low viscosity,can do brush coating,10Kg/set


performance features:
 BD426 desulfurization slurry circulating pump corrosion protective coating excellent chemical corrosion resistance
 With good performance in erosion resistant,cavitation resistant and impact resistant
 Impact resistant,with very high bonding strength to the metal.
 Without shrinkage after curing


product usage:
     BD426 desulfurization slurry circulating pump corrosion protective coating can excellent acid and alkaline.  Used in the large areas corrosion resistant protecting of the equipment.

How to use:
 1.  Surface treatment:Do coarsening treatment on the pending-repair surface,then clean it by cleaning agent.
 2.  Configure:According to the mass ratio A:B=5:1 or volume ratio A:B=3.5:1,make A and B two component mix uniformly,then use it up within specified operation time limit.
 3.  Coating:Make the mixed-up material be coating on the pending-repair part layer by layer,the first layer should be compacted,make it fully infiltrates with the substrates.If the next process needing machining,should set apart proper working allowance.
 4.  Curing:Cure for 24 hours at the temperature of 20～25℃ before putting into using,if the temperature is low,should heat it up or prolong curing time to promote the curing.


performance index:

BD426 desulfurizing slurry recycle pump anticorrosion protective coating  Physical mechanical properties table
color	physical state	density(g/cm3)	compressive strength(Mpa) GB/1041-2008	shear strength(Mpa) GB/7124-2008	tensile strength(Mpa) GB6329-2009	bending strength(Mpa) GB1042-1999	hardness(Shore D) ASTM-D-2556
gray	semi-fluid	1.11	90	17	35	43	83

BD426 The curing characteristics(test condition:temperature:20～25℃,relative humidity:55)
operational time limit(min)	curing time	need curing time before full load operation	working temperature(℃)	the highest temperature resistant(℃)
30～60	room temperature:24h or room temperature:2h+80℃:1h	48h	-60～150	160

Special version:
1. This parameter is for laboratory conditions,due to the actual working condition is more complex,suggest users do pretest according to actual working condition
2. When the environment temperature is below  15℃,the curing time will prolong,should take proper heating measure
3. When the environment temperature is more than 25℃ or the mixing quantity is too large,the curing speed will expedite,should properly shorten the application time of coating after mixing.

Transportation storage:
Sealed storage in the cool and dry place.The warranty period is 2 years.Avoid placing it upside down,knocking against and transporting it as a non-dangerous product during transportation.

Product packaging photo of BD426 desulfuration slurry circulating pump repair chemical corrosion wear resistant ceramic coating: